BU-213: Cycle Performance of NiCd, NiMH and Li-ion

Learn about the rugged old NiCd and compare with NiMH and Li-ion.

To compare older and newer battery systems, Cadex tested a large volume of nickel-cadmium, nickel-metal-hydride and lithium ion batteries used in portable for communication devices. Preparations included an initial charge, followed by a regime of full discharge/charge cycles at a 1C rate. The following tables show the capacity in percent, DC resistance measurement and self-discharge obtained from time to time by reading the capacity loss incurred during a 48-hour rest period. The tests were carried out on the Cadex 7000 Series battery analyzers.


In terms of life cycling, NiCd is the most enduring battery. Figure 1  illustrates capacity, internal resistance and self-discharge of a 7.2V, 900mA pack with standard NiCd cell. The internal resistance stayed low at 75mΩ and the self-discharge was stable. Due to time constraints, the test was terminated after 2,300 cycles.

This battery receives a grade “A” rating for almost perfect performance in terms of minimal capacity loss when cycling with a 100 percent DoC and rock-solid internal resistance over the entire test. NiCd is the only chemistry that can be ultra-fast charged with little stress. Due to its safe operation, NiCd remains the preferred choice of battery onboard aircrafts.

Figure 1: Performance of standard NiCd. (7.2V, 900mAh)
This battery receives an “A” rating for stable capacity; low internal resistance and moderate self-discharge over many cycles.
Courtesy of Cadex

The ultra-high-capacity nickel-cadmium offers up to 60 percent higher specific energy compared to the standard version, but this comes at the expense of reduced cycle life. Figure 2 observes a steady drop of capacity during 2,000 cycles, a slight increase in internal resistance and a notable rise in self-discharge after 1,000 cycles.

Figure 2: Performance of ultra-high-capacity NiCd. (6V, 700mAh)
This battery offers higher specific energy than the standard version at the expense of reduced cycle life.
Courtesy of Cadex


Figure 3 examines NiMH, a battery that offers high specific energy but loses capacity after the 300-cycle mark. There is also a rapid increase in internal resistance after a cycle count of 700 and a rise in self-discharge after 1000 cycles. The test was done on an older generation NiMH.

Figure 3: Performance of NiMH. (6V, 950mAh)
This battery offers good performance at first but past 300 cycles, the capacity, internal resistance and self-discharge start to increase rapidly.
Courtesy of Cadex


Figure 4 examines the capacity fade of a modern Li-ion Power Cell at a 2A, 10A, 15A and 20A discharge. Stresses increase with higher load currents and this also applies to fast-charging. The rugged Power Cell is more enduring than the more delicate Energy Cell. (See BU-401a: Fast and Ultrafast Chargers.)

Li-ion manufacturers often do not specify the rise of internal resistance and self-discharge as a function of cycling. Advancements have been made with electrolyte additives to keep the resistance low through most of the battery life. The self-discharge of Li-ion is normally low but it can increase if misused or if exposed to deep discharges. (See BU-802b: What does Elevated Self-discharge do?).

Figure 4: Cycle characteristics of IHR18650C by E-One Moli. (3.6V, 2,000mA)
18650 Power Cell was charged with 2A and discharged at 2, 10, 15 and 20A. The internal resistance and self-discharge are N/A.
Courtesy of E-One Moli Energy

Batteries tested in a laboratory tend to provide better results than in the field. Elements of stress in everyday use do not always transfer well into test laboratory. Aging plays a minimal role in a lab because the batteries are cycled over a period of a few months rather than the expected service life of several years. The temperature is often moderate and the batteries are charged under controlled charging condition and with approved chargers. 

The load signature also plays a role, and all batteries were discharged with a DC load. Batteries tend to deliver lower cycle life if discharged with pulses. (See BU-501: Basics About Discharging.) Do not overstress a battery as this will shorten the life. If a battery must repeatedly be loaded at peak currents, increase the Ah rating.

Last updated 2016-04-01

*** Please Read Regarding Comments ***

Comments are intended for "commenting," an open discussion amongst site visitors. Battery University monitors the comments and understands the importance of expressing perspectives and opinions in a shared forum. However, all communication must be done with the use of appropriate language and the avoidance of spam and discrimination.

If you have a question, require further information, have a suggestion or would like to report an error, use the "contact us" form or email us at: BatteryU@cadex.com. While we make all efforts to answer your questions accurately, we cannot guarantee results. Neither can we take responsibility for any damages or injuries that may result as a consequence of the information provided. Please accept our advice as a free public support rather than an engineering or professional service.

Or Jump To A Different Article

Basics You Should Know
The Battery and You
Batteries as Power Source

Comments (1)

On January 13, 2018 at 12:19pm
Walter Saucier wrote:

Which Panasonic AA battery has a lower internal resistance -eneloop Pro or regular eneloopn 2000 mAh?